Thanks to the heat resistance properties (up to 130 °C / 266 °F) of nyloprint® WS 152/175 metal based plates, they are ideally suited for hot moulding to produce rubber clichés.
Suitable equipment
The nyloprint® WS plates can be processed with nyloprint® processing equipment and all similar devices. The nyloprint® WS-S Digital can be used with all IR-laser systems suitable for imaging letterpress plates. For washout the use of brushes in the washer is recommended.
Washout medium
For washout only pure tap water is needed.
Processing information
A detailed description of the individual platemaking steps, as well as detailed information about processing and storing can be found in the nyloprint® User Guide.
High quality standard
nyloprint® printing plates are manufactured according to DIN ISO 9001, DIN ISO 14001 and DIN ISO 50001 standards and requirements. This process guarantees our customers consistent high quality products and services.
Specifications
Base Material
steel 0.3 mm (0.012“)
Colour of raw plate
red
Total thickness (mm) (inch)
1.52 (0.060")
Plate hardness (Shore D)
75
Relief depth (mm) (inch)
1.20 (0.047")
Tonal range (%)
2–95
at screen ruling of
60 l/cm (150 lpi)
Fine line width (down to μm)
100
Isolated dot diameter (down to μm)
200
Distortion factor (mm) (inch)
8.61 (0.339")
Main exposure (min) to be tested
5
Washout time
5.5
Washout temperature
45°C / 113° F
Drying time at 80°C / 176°F (min)
180
Post exposure (min)
2
Base Material
steel
Colour of raw plate
red
Total thickness (mm) (inch)
1.75 (0.069")
Plate hardness (Shore D)
71
Relief depth (mm) (inch)
1.45 (0.057")
Tonal range (%)
2–95
at screen ruling of
60 l/cm (150 lpi)
Fine line width (down to μm)
100
Isolated dot diameter (down to μm)
200
Distortion factor (mm) (inch)
10.05 (0.396")
Main exposure (min) to be tested
to be tested
Washout time
7
Washout temperature
45°C / 113° F
Drying time at 80°C / 176°F (min)
180
Post exposure (min)
2
Base Material
steel
Colour of raw plate
red
Total thickness (mm) (inch)
0.58 (0.023")
Plate hardness (Shore D)
84
Relief depth (mm) (inch)
0.32 (0.013")
Tonal range (%) at screen ruling
2 – 95 at 60 l/cm (150 lpi)
Fine line width (down to μm)
100
Isolated dot diameter (down to μm)
200
Distortion factor (mm) (inch)
3.02 (0.119")
Main exposure (min)
to be tested
Washout at 30°C / 86° F (min)
1.0 – 3.5
Drying time at 80°C / 176°F (min)
15
Post exposure (min)
2
Base Material
steel
Colour of raw plate
red
Total thickness (mm) (inch)
0.73 (0.029")
Plate hardness (Shore D)
77
Relief depth (mm) (inch)
0.46 (0.018")
Tonal range (%) at screen ruling
2 – 95 at 60 l/cm (150 lpi)
Fine line width (down to μm)
100
Isolated dot diameter (down to μm)
200
Distortion factor (mm) (inch)
3.85 (0.152")
Main exposure (min)
1.0 – 5.0
Washout at 30°C / 86° F (min)
1.0 – 3.5
Drying time at 80°C / 176°F (min)
15
Post exposure (min)
2
Base Material
steel
Colour of raw plate
red
Total thickness (mm) (inch)
0.83 (0.033")
Plate hardness (Shore D)
76
Relief depth (mm) (inch)
0.56 (0.022")
Tonal range (%) at screen ruling
2 – 95 at 60 l/cm (150 lpi)
Fine line width (down to μm)
100
Isolated dot diameter (down to μm)
200
Distortion factor (mm) (inch)
4.49 (0.177")
Main exposure (min)
1.0 – 5.0
Washout at 30°C / 86° F (min)
1.0 – 3.5
Drying time at 80°C / 176°F (min)
15
Post exposure (min)
2
Base Material
steel
Colour of raw plate
red
Total thickness (mm) (inch)
0.94 (0.037")
Plate hardness (Shore D)
73
Relief depth mm) (inch)
0.67 (0.026")
Tonal range (%) at screen ruling
2 – 95 at 60 l/cm (150 lpi)
Fine line width (down to μm)
100
Isolated dot diameter (down to μm)
200
Distortion factor (mm) (inch)
5.19 (0.204")
Main exposure (min)
1.0 – 5.0
Washout at 30°C / 86° F (min)
1.0 – 3.5
Drying time at 80°C / 176°F (min)
15
Post exposure (min)
2