Product Overview
-
Solvent Plate
-
Round Top Dot
-
Coated Kraft Liner
-
Uncoated Kraft Liner
-
Coated Test Liner
-
Uncoated Test Liner
-
Water Based Ink
-
Digital
- Superior printing quality with sharper images, more open intermediate depths
- Increased productivity and data transfer without loss of quality due to digital workflow
- Consistency in quality when repeating plate processing
- Cost-effective and more environmentally friendly in processing, as no film is required
Benefits
- Perfect area coverage, particularly on low cost liners
- Very good ink transfer
- Good intermediate depths
- Excellent print results, particularly in solid areas
- Superior printing performance in line work
- Suitable for screen work
- Superior durability and long lasting lifetime
- Suitable for standard equipment – no additional investment necessary
- Established technology – no additional training required
- Easy handling – clean and fast processing
- Reduced plate cleaning cycles
Suitable equipment
The nyloflex® FSC Digital can be processed with nyloflex® processing equipment and all similar devices. The nyloflex® FSC Digital can be used with all laser systems suitable for imaging flexo printing plates.
Printing inks Suitable
For all water based printing inks.
Washout solvents
Especially good results are achieved with nylosolv® washout solvents. nylosolv® can be distilled and reused.
Processing information
A detailed description of the individual platemaking steps, as well as detailed information about processing and storing can be found in the nyloflex® User Guide.
High quality standard
nyloflex® printing plates are manufactured according to DIN ISO 9001, DIN ISO 14001 and DIN ISO 5001 standards and requirements. This process guarantees our customers consistent high quality products and services.
Specifications
Base material
polyester film
Color of raw plate
orange, with black LAMS layer
Total thickness (mm) (inch)
2.84 (0.112")
Hardness acc. to DIN 53505
26
Plate hardness (Shore A)
35
Recommended relief depth (mm)
0.9–1.2
Tonal range (%)
3–95
At screen ruling (l/cm)
32 l/cm (80 lpi)
Fine line width (down to μm)
100
Isolated dot diameter (down to μm)
200
Back exposure (s)
50–70
Main exposure (min)
10–14
Washout speed (mm/min)
130–150
Drying time at 60°C / 140°F (h)
3.0
Post exposure UV-A (min)
10
Light finishing UV-C (min)
8–12
Base material
polyester film
Color of raw plate
orange, with black LAMS layer
Total thickness (mm) (inch)
3.18 (0.125")
Hardness acc. to DIN 53505
26
Plate hardness (Shore A)
33
Recommended relief depth (mm)
0.9–1.2
Tonal range (%)
3–95
At screen ruling (l/cm)
32 l/cm (80 lpi)
Fine line width (down to μm)
300
Isolated dot diameter (down to μm)
750
Back exposure (s)
50–100
Main exposure (min)
10–14
Washout speed (mm/min)
130–140
Drying time at 60°C / 140°F (h)
3.0
Post exposure UV-A (min)
10
Light finishing UV-C (min)
8–12
Base material
polyester film
Color of raw plate
orange, with black LAMS layer
Total thickness (mm) (inch)
3.94 (0.155")
Hardness acc. to DIN 53505
26
Plate hardness (Shore A)
28
Recommended relief depth (mm)
1.0–1.5
Tonal range (%)
3–95
At screen ruling (l/cm)
32 l/cm (80 lpi)
Fine line width (down to μm)
300
Isolated dot diameter (down to μm)
750
Back exposure (s)
50–100
Main exposure (min)
10–14
Washout speed (mm/min)
90–100
Drying time at 60°C / 140°F (h)
3.0
Post exposure UV-A (min)
10
Light finishing UV-C (min)
8–12
Base material
polyester film
Color of raw plate
orange, with black LAMS layer
Total thickness (mm) (inch)
4.32 (0.170")
Hardness acc. to DIN 53505
26
Plate hardness (Shore A)
27
Recommended relief depth (mm)
1.2–1.7
Tonal range (%)
3–95
At screen ruling (l/cm)
24 l/cm (60 lpi)
Fine line width (down to μm)
300
Isolated dot diameter (down to μm)
750
Back exposure (s)
50–100
Main exposure (min)
10–14
Washout speed (mm/min)
70–90
Drying time at 60°C / 140°F (h)
3.5
Post exposure UV-A (min)
10
Light finishing UV-C (min)
8–12
Base material
polyester film
Color of raw plate
orange, with black LAMS layer
Total thickness (mm) (inch)
4.70 (0.185")
Hardness acc. to DIN 53505
26
Plate hardness (Shore A)
27
Recommended relief depth (mm)
1.2–1.7
Tonal range (%)
3–95
At screen ruling (l/cm)
24 l/cm (60 lpi)
Fine line width (down to μm)
300
Isolated dot diameter (down to μm)
750
Back exposure (s)
50–100
Main exposure (min)
10–14
Washout speed (mm/min)
70–90
Drying time at 60°C / 140°F (h)
3.5
Post exposure UV-A (min)
10
Light finishing UV-C (min)
8–12
Base material
polyester film
Color of raw plate
orange, with black LAMS layer
Total thickness (mm) (inch)
5.00 (0.197")
Hardness acc. to DIN 53505
26
Plate hardness (Shore A)
27
Recommended relief depth (mm)
1.8–2.8
Tonal range (%)
3–95
At screen ruling (l/cm)
24 l/cm (60 lpi)
Fine line width (down to μm)
300
Isolated dot diameter (down to μm)
750
Back exposure (s)
90-150
Main exposure (min)
10–14
Washout speed (mm/min)
50–60
Drying time at 60°C / 140°F (h)
4.0
Post exposure UV-A (min)
10
Light finishing UV-C (min)
8–12
Base material
polyester film
Color of raw plate
orange, with black LAMS layer
Total thickness (mm) (inch)
5.50 (0.217")
Hardness acc. to DIN 53505
26
Plate hardness (Shore A)
26
Recommended relief depth (mm)
2.0–3.0
Tonal range (%)
3–95
At screen ruling (l/cm)
24 l/cm (60 lpi)
Fine line width (down to μm)
300
Isolated dot diameter (down to μm)
750
Back exposure (s)
120–160
Main exposure (min)
10–14
Washout speed (mm/min)
50–60
Drying time at 60°C / 140°F (h)
4.0
Post exposure UV-A (min)
10
Light finishing UV-C (min)
8–12
Base material
polyester film
Color of raw plate
orange, with black LAMS layer
Total thickness (mm) (inch)
6.00 (0.236")
Hardness acc. to DIN 53505
26
Plate hardness (Shore A)
26
Recommended relief depth (mm)
2.0–3.0
Tonal range (%)
3–95
At screen ruling (l/cm)
24 l/cm (60 lpi)
Fine line width (down to μm)
300
Isolated dot diameter (down to μm)
750
Back exposure (s)
250–300
Main exposure (min)
10–14
Washout speed (mm/min)
40–60
Drying time at 60°C / 140°F (h)
4.0
Post exposure UV-A (min)
10
Light finishing UV-C (min)
8–12
Base material
polyester film
Color of raw plate
orange, with black LAMS layer
Total thickness (mm) (inch)
6.35 (0.250")
Hardness acc. to DIN 53505
26
Plate hardness (Shore A)
26
Recommended relief depth (mm)
2.0–3.0
Tonal range (%)
3–95
At screen ruling (l/cm)
24 l/cm (60 lpi)
Fine line width (down to μm)
300
Isolated dot diameter (down to μm)
750
Back exposure (s)
250–300
Main exposure (min)
10–14
Washout speed (mm/min)
40–60
Drying time at 60°C / 140°F (h)
4.0
Post exposure UV-A (min)
10
Light finishing UV-C (min)
8–12