Product Overview
-
Solvent Plate
-
Coated Kraft Liner
-
Uncoated Kraft Liner
-
Coated Test Liner
-
Uncoated Test Liner
-
Water Based Ink
-
Analogue
Benefits
High plate hardness for reliable print quality
- Suitable for a broad range of substrates
- Very good and consistent ink transfer with excellent area coverage
- High solid density and minimum dot gain in the halftones
- intermediate depths with excellent contour definition
Efficient handling and superior durability
- Convenient plate processing with short exposure times
- High print run stability due to superior resistance against mechanical stress
- Long lifetime due to robust and durable material
- Reduced cleaning cycles due to special surface properties
Suitable equipment
The nyloflex® FHC can be processed with nyloflex® processing equipment and all similar devices.
Printing inks
Suitable for all water based and alcohol based printing inks (ethyl acetate content preferably below 15%, ketone content preferably below 5%).
Washout solvents
Especially good results are achieved with nylosolv® washout solvents. nylosolv® can be distilled and reused.
Processing information
A detailed description of the individual platemaking steps, as well as detailed information about processing and storing can be found in the nyloflex® User Guide.
High quality standard
nyloflex® printing plates are manufactured according to DIN ISO 9001, DIN ISO 14001 and DIN ISO 5001 standards and requirements. This process guarantees our customers consistent high quality products and services.
Specifications
Base material
polyester foil
Color of raw plate
orange
Total thickness (mm) (inch)
3.94 (0.155")
Hardness acc. to DIN 53505
40
Plate hardness (Shore A)
41
Recommended relief depth (mm)
1.0 – 1.5
Tonal range (%)
3 – 90
At screen ruling (l/cm)
48
Fine line width (down to μm)
300
Isolated dot diameter (down to μm)
750
Back exposure (s)
50 – 100
Main exposure (min)
8 – 18
Washout speed (mm/min)
70 – 100
Drying time at 60°C / 140°F (h)
3.0
Post exposure UV-A (min)
10
Light finishing UV-C (min)
10 – 15