Product Overview
-
Solvent Plate
-
Coated Kraft Liner
-
Uncoated Kraft Liner
-
Coated Test Liner
-
Uncoated Test Liner
-
Water Based Ink
-
Analogue
Benefits
- Especially for printing on coarse corrugated fluted board, with uncoated and half coated papers
- Ideal for retail packages with simple designs
- Optimised for use in inline corrugated print production
- Very good ink transfer with excellent area coverage and high solid density
- Perfect adaptation to corrugated board surfaces reduces washboard effect
- Less plate cleaning due to special surface properties
- Extremely robust and durable material thus
- high print run stability
- excellent storage capability
- low swelling characteristic
- high resistance to ozone
Suitable equipment
The nyloflex® FCC can be processed with nyloflex® processing equipment and all similar devices.
Printing inks
Suitable for all water based and alcohol based printing inks (ethyl acetate content preferably below 15%, ketone content preferably below 5%).
Washout solvents
Especially good results are achieved with nylosolv® washout solvents. nylosolv® can be distilled and reused.
Processing information
A detailed description of the individual platemaking steps, as well as detailed information about processing and storing can be found in the nyloflex® User Guide.
High quality standard
nyloflex® printing plates are manufactured according to DIN ISO 9001, DIN ISO 14001 and DIN ISO 5001 standards and requirements. This process guarantees our customers consistent high quality products and services.
Specifications
Base material
polyester film
Color of raw plate
orange
Total thickness (mm) (inch)
6.35 (0.250")
Hardness acc. to DIN 53505
30
Plate hardness (Shore A)
30
Recommended relief depth (mm)
2.2–3.0
Tonal range (%)
3–95
At screen ruling (l/cm)
24 l/cm (60 lpi)
Fine line width (down to μm)
300
Isolated dot diameter (down to μm)
1000
Back exposure (s)
250–300
Main exposure (min)
8–18
Washout speed (mm/min)
60–70
Drying time at 60°C / 140°F (h)
4.0
Post exposure UV-A (min)
10
Light finishing UV-C (min)
8–12